Hostaform® C 52021
聚甲醛（POM）共聚物
Celanese Corporation
產品說明:
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 06-002
POM copolymer
Extremely easy flowing Injection molding type for very thin-walled
precision molded parts with unfavourite flow-path-wallthickness
relation; permits processing at reduced temperature and also shorter
cycle times; for mechanical lower requirements; good chemical
resistance to solvents, fuel and strong alkalis as well as good
hydrolysis resistance; high resistance to thermal and oxidative
degradation.
Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470
UL-registration in natural a thickness more than 0.81 mm, in black a
thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B
for a thickness of 1.5 mm, electrical 105°C, mechanical 90°C
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more
than 1 mm.
Ranges of applications: For very thin-walled precision molded parts
with unfavourite flow-path-wallthickness relation; permits
processing at reduced temperature and also shorter cycle times.
FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
|
供貨地區 |
|
|||||
|
特性 |
|
|||||
|
用途 |
|
|||||
|
機構評級 |
|
|||||
|
RoHS 合規性 |
|
|||||
|
加工方法 |
|
|||||
|
多點數據 |
|
|||||
|
樹脂ID (ISO 1043) |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|||
|
密度 |
1.41 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
39.0 |
cm3/10min |
ISO 1133 |
|||
|
收縮率 |
|
|
ISO 294-4 |
|||
|
橫向流量 |
1.8 |
% |
|
|||
|
流量 |
1.9 |
% |
|
|||
|
吸水率 (飽和, 23°C) |
0.65 |
% |
ISO 62 |
|||
|
機械性能 |
額定值 |
單位制 |
測試方法 |
|
拉伸模量 |
3000 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應力 (屈服) |
65.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應變 (屈服) |
7.0 |
% |
ISO 527-2/1A/50 |
|
標稱拉伸斷裂應變 |
15 |
% |
ISO 527-2/1A/50 |
|
拉伸蠕變模量 |
|
|
ISO 899-1 |
|
1 hr |
2500 |
MPa |
|
|
1000 hr |
1300 |
MPa |
|
|
彎曲模量 (23°C) |
2800 |
MPa |
ISO 178 |
|
沖擊性能 |
額定值 |
單位制 |
測試方法 |
|
簡支梁缺口沖擊強度 |
|
|
ISO 179/1eA |
|
-30°C |
5.0 |
kJ/m2 |
|
|
23°C |
5.0 |
kJ/m2 |
|
|
簡支梁無缺口沖擊強度 |
|
|
ISO 179/1eU |
|
-30°C |
100 |
kJ/m2 |
|
|
23°C |
100 |
kJ/m2 |
|
|
熱性能 |
額定值 |
單位制 |
測試方法 |
|
熱變形溫度 (1.8 MPa, 未退火) |
106 |
°C |
ISO 75-2/A |
|
熔融溫度 3 |
166 |
°C |
ISO 11357-3 |
|
線形熱膨脹系數 - 流動 |
1.1E-4 |
cm/cm/°C |
ISO 11359-2 |
|
|