| 規格級別 | 注塑 其它 其它 | 外觀顏色 | |
| 該料用途 | |||
| 備注說明 | 特性：玻璃30%強化，高流動。 | ||
| 加工條件 |
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | ||||
| 基本性能 | 吸水率 | 23℃，24小時 |
|
% | ||||
| 物理性能 | 比重 | ASTM D-792 |
|
|||||
| 機械性能 | IZOD沖擊強度 | 無缺口1/8，23℃ |
|
kg·cm/cm2 | ||||
| 撓曲強度 | 80℃ | ASTM D-790 |
|
Kg/cm2 | ||||
| 抗剪強度 | 23℃ | ASTM D-732 |
|
Kg/cm2 | ||||
| 斷裂伸長率 | 80℃ | ASTM D-638 |
|
% | ||||
| 斷裂伸長率 | 23℃ | ASTM D-638 |
|
% | ||||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
R-標度 | ||||
| 洛氏硬度 | 23℃ | ASTM D-785 |
|
M-標度 | ||||
| 抗拉屈服強度 | 80℃ | ASTM D-638 |
|
Kg/cm2 | ||||
| 撓曲模量 | -40℃ | ASTM D-790 |
|
Kg/cm2 | ||||
| 撓曲強度 | 23℃ | ASTM D-790 |
|
Kg/cm2 | ||||
| 壓縮強度 | -40℃ | ASTM D-695 |
|
Kg/cm2 | ||||
| 壓縮強度 | 80℃ | ASTM D-695 |
|
Kg/cm2 | ||||
| 撓曲模量 | 80℃ | ASTM D-790 |
|
Kg/cm2 | ||||
| 斷裂伸長率 | -40℃ | ASTM D-638 |
|
% | ||||
| 撓曲模量 | 23℃ | ASTM D-790 |
|
Kg/cm2 | ||||
| 撓曲強度 | -40℃ | ASTM D-790 |
|
Kg/cm2 | ||||
| 抗剪強度 | 80℃ | ASTM D-792 |
|
Kg/cm2 | ||||
| 壓縮強度 | 23℃ | ASTM D-695 |
|
Kg/cm2 | ||||
| 抗拉屈服強度 | -40℃ | ASTM D-638 |
|
Kg/cm2 | ||||
| IZOD沖擊強度 | V-缺口1/2，-40℃ | ASTM D-256 |
|
kg·cm/cm2 | ||||
| 泰伯磨耗量 | (1000g,CS-17)23℃ | ASTM D-1044 |
|
mg/1000次 | ||||
| IZOD沖擊強度 | 無缺口1/8，-40℃ |
|
kg·cm/cm2 | |||||
| IZOD沖擊強度 | V-缺口1/2，23℃ | ASTM D-256 |
|
kg·cm/cm2 | ||||
| 抗拉屈服強度 | 23℃ | ASTM D-638 |
|
Kg/cm2 | ||||
| 電氣性能 | 抗電弧性 | 1/8" | ASTM D-495 |
|
秒 | |||
| 介電常數 | 50Hz | ASTM D-150 |
|
|||||
| 體積電阻率 | ASTM D-257 |
|
Ω.cm | |||||
| 損耗因數 | 50Hz | ASTM D-150 |
|
|||||
| 損耗因數 | 103Hz | ASTM D-150 |
|
|||||
| 介電常數 | 103Hz | ASTM D-150 |
|
|||||
| 損耗因數 | 106Hz | ASTM D-150 |
|
|||||
| 介電強度 | 1/8" | ASTM D-149 |
|
KV/mm | ||||
| 介電常數 | 106Hz | ASTM D-150 |
|
|||||
| 熱性能 | 導熱系數 |
|
Kcal/m·hr·℃ | |||||
| 熔點 | 差示掃描測熱計DSC |
|
℃ | |||||
| 線性熱膨脹系數 | ASTM D-696 |
|
×10-5cm/cm/℃ | |||||
| 熱撓曲溫度 | 4.6kg/cm2 | ASTM D-648 |
|
℃ | ||||
| UL-94抗燃級 | UL 94 |
|
||||||
| 熱撓曲溫度 | 18.6kg/cm2 | ASTM D-648 |
|
℃ | ||||
| 比熱 |
|
Cal/g·℃ | ||||||
| 其它性能 | 強化含量 |
|
WT% | |||||