| PC/ABS C1200 美國通用電氣公司 物性數據 |
| 規格級別： | --- | 外觀顏色： | --- |
| 用途概述： | --- | ||
| 備注說明： | 特性：耐高溫及沖擊 | ||
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.15 | --- |
| 吸水率 | --- | ASTM D-570 | - | % | |
| 模具收縮率 | 3.2mm | ASTM D-955 | 5-7 | E-3 | |
| 機械性能 | 拉伸強度(屈伏點) | --- | ASTM D-638 | 61 | Mpa |
| 拉伸模量 | --- | ASTM D-638 | 2274 | Mpa | |
| 彎曲強度 | --- | ASTM D-790 | 88 | Mpa | |
| 彎曲模量 | --- | ASTM D-790 | 2343 | Mpa | |
| 沖擊強度缺口 | 23℃ | ASTM D-256 | 640 | J/m | |
| 洛氏硬度 | --- | ASTM D-785 | - | R | |
| 電氣性能 | 拉伸率(斷裂點) | --- | ASTM D-638 | 150 | % |
| 損耗因數 | 1MHz | ASTM D-150 | - | --- | |
| 介電常數 | 1MHz | ASTM D-150 | - | --- | |
| 體積電阻 | --- | ASTM D-257 | - | Ohm-cm | |
| 表面電阻 | --- | ASTM D-257 | - | Ohm-cm | |
| 熱 性 能 | 阻燃性 | --- | UL-94 | HB | --- |
| 阻燃性 | --- | UL-94 | 1.6 | mm | |
| 熱變形溫度 | 0.45Mpa | ASTM D-648 | 129 | ℃ | |
| 熱變形溫度 | 1.8Mpa | ASTM D-648 | 112 | ℃ | |
| 維卡軟化點 | --- | ASTM D-1525 | - | ℃ | |
| 線膨脹系數 | 1/℃ | E-831 | 7.2E-05 | --- | |
| UL長期使用溫度 | 含沖擊 | UL-746B | 60 | ℃ | |
| UL長期使用溫度 | 無沖擊 | UL-746B | 60 | ℃ | |
PC/ABS結合了兩種材料的優異特性，
ABS材料的成型性和PC的機械性、沖擊強度和耐溫、抗紫外線（UV）等性質，可廣泛使用在汽車內部零件、事務機器、通信器材、家電用品及照明設備上。[1][2]
典型應用范圍:手機外殼、計算機和商業機器殼體、電器設備、草坪園藝機器、汽車零件儀表板、內部裝修以及車輪蓋）。
注塑模工藝條件:干燥處理：加工前的干燥處理是必須的。濕度應小于0.04%，建議干燥條件為90~110C，2~4小時。熔化溫度： 230~300C。模具溫度：50~100C。注射壓力：取決于塑件。注射速度：盡可能地高。
化學和物理特性: PC/ABS具有PC和ABS兩者的綜合特性。例如ABS的易加工特性和PC的優良機械特性和熱穩定性。二者的比率將影響PC/ABS材料的熱穩定性。PC/ABS這種混合材料還顯示了優異的流動特性。收縮率在0.5%左右。
二、PC/ABS是一種通過混煉后合成的改性工程塑料。這種改性塑料比單純的PC和ABS性能更好，例如：抗沖擊性提高，耐熱性提高，硬度提高等等.
PC/ABS塑料 特點：
1、綜合性能較好,沖擊強度較高,化學穩定性,電性能良好.
2、與372有機玻璃的熔接性良好,制成雙色塑件,且可表面鍍鉻,噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強、透明等級別。
4、流動性比HIPS差一點，比PMMA、PC等好，柔韌性好。