PA66 - CM3001G-30 物性表
日本東麗工業株式會社PA66 CM3001G-30 物性數據 |
①原料描述部分 |
|||
規格級別： |
注塑級 |
外觀顏色： |
--- |
用途概述： |
一般用途 |
||
備注說明： |
特性：玻纖增強30% |
||
②原料技術數據 |
|||||||||
性能項目 |
試驗條件[狀態] |
測試方法 |
|
數據單位 |
|||||
基本性能 |
吸水率 |
23℃ |
ASTM D-570 |
|
% |
||||
物理性能 |
比重 |
--- |
ASTM D-792 |
|
--- |
||||
泰伯磨耗量 |
(1000g,CS-17)23℃ |
ASTM D-1044 |
|
mg/1000次 |
|||||
機械性能 |
洛氏硬度 |
23℃ |
ASTM D-785 |
|
M-標度 |
||||
壓縮強度 |
80℃ |
ASTM D-695 |
|
Kg/cm2 |
|||||
抗剪強度 |
23℃ |
ASTM D-732 |
|
Kg/cm2 |
|||||
抗剪強度 |
80℃ |
ASTM D-732 |
|
Kg/cm2 |
|||||
IZOD沖擊強度 |
-40℃，V缺口1/2 |
ASTM D-256 |
|
kg・cm/cm |
|||||
IZOD沖擊強度 |
23℃，V-缺口1/2 |
ASTM D-256 |
|
kg・cm/cm |
|||||
IZOD沖擊強度 |
-40℃ |
--- |
|
kg・cm/cm2 |
|||||
IZOD沖擊強度 |
23℃，無缺口1/8 |
--- |
|
kg・cm/cm2 |
|||||
洛氏硬度 |
23℃ |
ASTM D-785 |
|
R-標度 |
|||||
抗拉屈服強度 |
-40℃ |
ASTM D-638 |
|
Kg/cm2 |
|||||
抗拉屈服強度 |
23℃ |
ASTM D-638 |
|
Kg/cm2 |
|||||
抗拉屈服強度 |
80℃ |
ASTM D-638 |
|
Kg/cm2 |
|||||
斷裂伸長率 |
-40℃ |
ASTM D-638 |
|
% |
|||||
斷裂伸長率 |
23℃ |
ASTM D-638 |
|
% |
|||||
斷裂伸長率 |
80℃ |
ASTM D-638 |
|
% |
|||||
撓曲強度 |
-40℃ |
ASTM D-790 |
|
Kg/cm2 |
|||||
撓曲強度 |
23℃ |
ASTM D-790 |
|
Kg/cm2 |
|||||
撓曲強度 |
80℃ |
ASTM D-790 |
|
Kg/cm2 |
|||||
撓曲模量 |
-40℃ |
ASTM D-790 |
|
Kg/cm2 |
|||||
撓曲模量 |
80℃ |
ASTM D-790 |
|
Kg/cm2 |
|||||
壓縮強度 |
-40℃ |
ASTM D-695 |
|
Kg/cm2 |
|||||
壓縮強度 |
23℃ |
ASTM D-695 |
|
Kg/cm2 |
|||||
電氣性能 |
體積電阻率 |
--- |
ASTM D-257 |
|
Ω.cm |
||||
介電強度 |
1/8" |
ASTM D-149 |
|
KV/mm |
|||||
介電常數 |
50Hz |
ASTM D-150 |
|
--- |
|||||
介電常數 |
103Hz |
ASTM D-150 |
|
--- |
|||||
介電常數 |
106Hz |
ASTM D-150 |
|
--- |
|||||
損耗因數 |
50Hz |
ASTM D-150 |
|
--- |
|||||
損耗因數 |
103Hz |
ASTM D-150 |
|
--- |
|||||
損耗因數 |
--- |
ASTM D-150 |
|
--- |
|||||
抗電弧性 |
1/8" |
ASTM D-495 |
|
s |
|||||
熱 性 能 |
UL-94抗燃級 |
1/16" |
UL 94 |
|
--- |
||||
熔點 |
--- |
差示掃描測熱計DSC |
|
℃ |
|||||
比熱 |
--- |
--- |
|
Cal/g・℃ |
|||||
導熱系數 |
--- |
--- |
|
Kcal/m・hr・℃ |
|||||
線性熱膨脹系數 |
--- |
ASTM D-696 |
|
×10-5cm/cm/℃ |
|||||
熱撓曲溫度 |
4.6kg/cm2 |
ASTM D-648 |
|
℃ |
|||||
熱撓曲溫度 |
18.6kg/cm2 |
ASTM D-648 |
|
℃ |
|||||
其它性能 |
強化含量 |
--- |
--- |
|
WT% |
||||